Welded steel pipe refers to the steel pipe with a joint on the surface which is welded after the steel strip or steel plate is bent and deformed into circular, square and other expected shapes. According to different welding methods, it can be divided into arc welded pipe, high frequency or low frequency resistance welded pipe, gas welded pipe, furnace welded pipe, Bondi pipe, a633 grade c structural, etc. According to the weld shape, it can be divided into straight welded pipe and spiral welded pipe. Electric welded steel pipes are mainly used in oil drilling and production, machinery manufacturing, etc.; furnace welded pipes can be used as water gas pipes, large-diameter straight seam welded pipes for high-pressure oil-gas transmission, etc.; spiral welded pipes are used for oil-gas transmission, pipe piles, piers, etc. Welded steel pipe has lower cost and higher production efficiency than seamless steel pipe.
A514gr.F high yield strength structural quality steel chemical composition%C: 0.10-0.20, Si: 0.15-0.35, Mn: 0.60-1.00, P max.: 0.035, S max.: 0.035, Ni: 0.70-1.00, Cr: 0.40-0.65, Mo: 0.15-0.25, V: 0.03-0.08, Cu: 0.15-0.50, B: 0.001-0.005The mechanical properties in the plate thickness (mm)T≤65Yield strength (≥Mpa): 690Tensile strength (Mpa):760-895Elongation in ≥, %: 18
The characteristic of niobium in a633 grade c structural etc. steel material is to increase the recrystallization temperature of austenite, so as to achieve the purpose of refining austenite grains. In general, the amount of niobium added in steel material is less than 0.05%, and the contribution of niobium above 0.05% to strengthening and toughening will no longer be obvious.
The related factors of a633 grade c structural steel plate cutting are mainly steel plate material, steel plate specific use and steel plate cutting requirements, so it can be said that there are many related factors. Different processing methods, such as finish machining and rough machining, choose different a633 grade c structural steel plate cutting methods. Wire cutting or plasma cutting is used for finishing and flame cutting is used for rough machining. Therefore, it can be concluded that the steel plate cutting methods selected under different processing methods are different.